ANALISIS FASA KRISTAL TERBENTUK PADA BAHAN GELAS METALIK BERBASIS ZIRKONIUM ANTARA SUHU 440 - 480?C

Authors

  • Fatimatul Munawaroh Program Studi PGSD, Fakultas Ilmu Pendidikan Universitas Trunojoyo Madura Jalan Raya Telang, PO BOX 2 Kamal, Bangkalan, Madura Telp. (031) 3012792, Faks. (031) 3011506
  • Triwikantoro Triwikantoro Jurusan Fisika, Institut Teknologi Sepuluh Nopember, Surabaya Kampus ITS Sukolilo, Surabaya 60111

DOI:

https://doi.org/10.12928/bfi-jifpa.v4i1%20&%202.237

Keywords:

gelas metalik berbasis zirkonium, pemanasan, suhu kristalisasi (T x)

Abstract

Telah dilakukan analisis fasa kristal yang terbentuk pada bahan gelas metalik berbasis zirkonium pada  suhuantara  440?  -  480?C.  Yaitu paduan  Zr53.1Cu23Ni18Al5.9, Zr65Cu17.5Ni10Al7.5  dan Zr69.5Cu12Ni11Al7.5  yang dipanaskan di  atas  suhu  kristalisasi (Tx)  antara 440?  -  480?C selama 1 jam. Sampel diuji difraksi sinar-X (XRD) sebelum dan sesudah dipanaskan untuk mengetahui fasa kristal yang terbentuk. Hasil identifikasi menunjukkan kristal yang terbentuk selama pemanasan terdiri dari ZrO2 (tetragonal) sebagai fasa dominan serta CuO dan NiO sebagai fasa minor. Selain itu terdapat fasa intermetalik Zr2Ni pada paduan  Zr65Cu17.5Ni10Al7.5. Ukuran kristal fasa kristal yang terbentuk dihitung dengan menggunakan persamaan Scherrer. Untuk fasa ZrO 2  tetragonal ukuran kristalnya berkisar antara 10-17 nm, ZrO2  kubik  antara 7-14 nm, CuO antara 14-30 nm, NiO antara 13-16 nm dan Zr2Ni antara 14-16 nm.

Downloads

Published

2013-04-01

Issue

Vol. 4 No. 1 & 2 (2012)

Section

Articles

License

Authors who publish with Berkala Fisika Indonesia : Jurnal Ilmiah Fisika, Pembelajaran dan Aplikasinya (BFI-JIFPA) agree to the following terms:

  1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License (CC BY-SA 4.0) that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal. 
  2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
  3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.

 


This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.