NANOKRISTALISASI SUPERKONDUKTOR (Bi,Pb)2 Sr2 CaCu 2O8+? DENGAN METODE PENCAMPURAN BASAH

Authors

  • Lydia Rohmawati Jurusan Fisika FMIPA Universitas Negeri Surabaya Gedung C9 Lt. 1, Ketintang, Surabaya 60231
  • _ Darminto Program Studi Magíster Fisika, Bidang Keahlian Material, Jurusan Fisika FMIPA, Institut Teknologi Sepuluh Nopember, Kampus ITS Sukolilo, Surabaya 60111

DOI:

https://doi.org/10.12928/bfi-jifpa.v4i1%20&%202.236

Keywords:

superkonduktor Bi-2212, nanokristalin, metode pencampuran basah, ukuran kristal, fraksi volume

Abstract

Bi2Sr2CaCu2O8+?(Bi-2212) merupakan bahan superkonduktif yang memiliki suhu kritis (Tc) sekitar 80 K. Pada penelitian ini dilakukan sintesis Bi-2212 murni dan Bi-2212 doping Pb dengan menggunakan metode pencampuran basah, untuk memperoleh ukuran kristal ?100 nm. Hasil sintesis dengan metode tersebut dikalsinasi dengan variasi suhu 400°C, 500°C dan 600°C selama satu jam serta 780°C selama 3 jam. Selanjutnya dilakukan sintering pada suhu 825°C dengan variasi waktu 1-5 jam. Hasil analisis dengan XRD menunjukkan bahwa Bi-2212 tanpa doping dengan sintering selama 1-5 jam memiliki ukuran kristal yang mencapai ~ 90 nm dengan fraksi volume 68%, sedangkan Bi-2212 doping Pb dengan sintering selama 1-3 jam menghasilkan ukuran kristalnya ~ 100 nm dengan fraksi volume mencapai 85%.

Downloads

Published

2013-04-01

Issue

Vol. 4 No. 1 & 2 (2012)

Section

Articles

License

Authors who publish with Berkala Fisika Indonesia : Jurnal Ilmiah Fisika, Pembelajaran dan Aplikasinya (BFI-JIFPA) agree to the following terms:

  1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License (CC BY-SA 4.0) that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal. 
  2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
  3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.

 


This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.